Ramming Mass Refractory Coating gunning material for metallurgical industry furnace lining
Product introduction
Aluminum silicate refractory mortar includes clay based refractory
mortar, mullite based refractory mortar, high alumina based refractory mortar and so on. accordingly, the matrix materials of aluminum silicate refractory mortars are clay clinker fines, sintered or fused mullite fines, high
alumina bauxite clinker fines, sintered or fused corundum fines. During making aluminum silicate mortar, some quantity of soft clay, bonder and additives are added into the matrix. The function of soft clay is to improve the workability of the
mortar, such as spread ability and adhesion ability, etc. Silica
micro powder can be used to replace soft clay to enhance
workability
Binding agent is required to improve the strength of aluminum silicate refractory mortar. There are two types of binders: 1) silicate series, i.e. water glass with different modulus
of (SiO2/Na2O). 2) Phosphate series, such as acidic aluminum phosphate and
polyphosphate, etc. The quantity of binders is decided by applications. Generally speaking, the more the binder, the higher the sintered binding strength. But at high temperature, the case is the opposite, because binders appear liquid phase at high temperature.
Physicochemical property of phosphate bonded aluminum silicate
refractory mortar
| Item | Clay mortar | High alumina mortar | Mullite mortar | Corundum mortar |
| RefractorinessºC ≥ | 1750 | 1790 | 1790 | 1850 |
| Rupture strength (Sintered) MPa ≥ | 5.9 (1200ºC) | 5.9 (1400ºC) | 5.9 (1500ºC) | 5.9 (1500ºC) |
| cementation time/ min | 1-2 | 1-2 | 1-2 | 1-2 |
| Granularity ≥0.5mm % | ≤1 | ≤1 | ≤1 | ≤1 |
| Al2O3 % ≥ | 45 | 70 | 70 | 90 |
| rupture under load temperature ºC ≥ | 1200 | 1300 | 1500 | 1700 |
Fire clay and high alumina based refractory gunning mass
| Item | Alumina magnesia castable | Alumina magnesia castable | High alumina castable |
| Application | Work lining | Work lining | Permanent lining |
| Al2O3 %≥ | 60 | 70 | 60 |
| MgO % ≥ | 12 | 10 | / |
| C % | / | / | / |
| Refractoriness ℃≥ | / | / | 1790 |
| RUL ℃ ≥ | 1200 | 1350 | / |
| LCR % (1400℃,2h) | 0~2 | 0~2 | 0~0.3 |
| Apparent porosity % ≤ | 23 | 25 | 18 |
| CCS MPa ≥ | 30 | 30 | 30 |
| Max. working temperature ℃ | 1700 | 1700 | 1650 |
|
|